High Performance Thermoset Materials
Engineered to Meet Challenging Production Requirements
NEW
Anchor-Seal Shore ‘A’ Flexible Polyurethane Elastomers
Soft Durometer / Flexible Urethanes for Hand Mixing or Dispensing Equipment. Shore ‘A’ Series is used for Mold Making and Casting Urethanes, i.e., Bumpers, Instrument Grips, Gaskets, Fixtures, Flexible Parts and Molds. Excellent Production-Oriented Elastomer.
Download
U2555A*
Transparent
Product #/Color
Working Time
100 Grams @77F
20 min.
Shore Hardness
55A
5-6 hours @77F
Shrinkage (in/in)
.006
Viscosity
@77F CPS
1300
Mix Ratio
Resin/Cure Wt. (Vol)
100:57
MSDS Sheets: U2055A - Pt A, U2055A - Pt B
Demold Time
Depending on Mass
ROHS Compliant, Superior Shock and Abrasion Resistance, Insensitive to Moisture, Easily Tinted
Download
U2060A*
Amber-Clear
Product #/Color
Working Time
100 Grams @77F
20 min.
Shore Hardness
60A
6-14 hours @77F
Shrinkage (in/in)
.007
Viscosity
@77F CPS
1300
Mix Ratio
Resin/Cure Wt. (Vol)
100:32
MSDS Sheets: U2060A - Pt A, U2060A - Pt B
Demold Time Depeending on Mass
ROHS Compliant, Superior Shock and Abrasion Resistance, Insensitieve to Moisture, Easily Tinted
Download
U2065A*
Transparent
Product #/Color
Working Time
100 Grams @77F
20 min.
Shore Hardness
65A
5-6 hours @77F
Shrinkage (in/in)
.006
Viscosity
@77F CPS
1100
Mix Ratio
Resin/Cure Wt. (Vol)
100:32
MSDS Sheets: U2065A - Pt A, U2065A - Pt B
Demold Time Depeending on Mass
ROHS Compliant, Superior Shock and Abrasion Resistance, Insensitieve to Moisture, Easily Tinted
Download
U2080AK*
Black
Product #/Color
Working Time
100 Grams @77F
20 min.
Shore Hardness
80A
6-8 hours @77F
Shrinkage (in/in)
.005
Viscosity
@77F CPS
1300
Mix Ratio
Resin/Cure Wt. (Vol)
100:44
MSDS Sheets: U2080AK - Pt A, U2080AK - Pt B
Demold Time Depeending on Mass
ROHS Compliant, Superior Shock and Abrasion Resistance, Insensitieve to Moisture, Easily Tinted
Download
U2095A*
Light Straw Clear
Product #/Color
Working Time
100 Grams @77F
20 min.
Shore Hardness
95A
4-6 hours @77F
Shrinkage (in/in)
.003
Viscosity
@77F CPS
1375
Mix Ratio
Resin/Cure Wt. (Vol)
100:34
MSDS Sheets: U2095A - Pt A, U2095A - Pt B
Demold Time Depeending on Mass
ROHS Compliant, Superior Shock and Abrasion Resistance, Insensitieve to Moisture, Easily Tinted
* Available in 10 minute working times for faster demolds
Pot life, gel time, cure time, and demold time vary depending on quantity mixed, thickness of casting and mold temperature. The use of heated molds is recommended i.e. 100F (38C). Warming the mold will accelerate demold and decrease cure times. Low temperatures will slow the curing and extend demold time. Hardness development progresses more slowly in the longer working time / longer pot life materials. Post-curing for 6-8 hrs @ 160-175F will accelerate development of properties. Impact strength and heat distortion properties improve when the casting is post cured. Aliphatic urethanes are UV resistant / non-yellowing. Read label, Technical Data Sheet and Safety Data Sheet before use.
Viscosity Chart
1 cps = Water
400 cps = #10 Motor Oil
1,000 cps = Castor Oil
3,500 cps = Karo Syrup
25,000 cps = Hershey's Chocolate Syrup